3003 for the AL-Mn series aluminum alloy, is the most widely used as a rust-proof aluminum, the strength of the aluminum alloy is not high (slightly higher than

Executive dip aluminum is pretreated work piece is immersed in the molten aluminum bath holding a certain time taken to penetrate the surface layer of aluminum.

Aluminum clad wood windows and doors made of aluminum alloy outdoor section dedicated mold extrusion profiles, the surface of fluorocarbon coating, can resist t

6063 Aluminum is AL-Mg-Si system with moderate strength alloy. It can be heat strengthened, industrial aluminum profile summary Mg and Si is the main alloying e

● Features and Scope: It belongs to Al-Zn-Mg-Cu based hard aluminum alloy rivets. Quenching artificial aging state can be riveting, high-strength rivets materi

In our building with aluminum windows and doors, curtain walls, the thickness of the level of the general requirements is anodized aluminum grade AA10, AA15 lev

Mechanical properties of aluminum 5B05: Shear strength τ (MPa): ≥157 Note: The heat does not strengthen the shear resistance of the wire ● Heat treatme

Windows and doors are an indispensable part of the living room. Today, the doors have gone through wood, steel, aluminum, steel doors and other four ages. Wood

5056 Al-Mg system for anti-rust aluminum alloy, non-heat strengthened. In addition to the chemical composition of the alloy is low manganese content, but substa

3003: For the processing need to have good formability, high corrosion resistance and good weld ability parts and components, or both of these performance requi

Mechanical Properties Tensile strength σb (MPa): ≥315Conditions yield strength σ0.2 (MPa): ≥160Elongation δ10 (%): ≥15Note: The ve

2011: cutting screws and require good mechanical processing products; 2014: applications requiring high strength and hardness (including temperature) of the oc

1050: food, chemical and brewing industry squeezed coil, various hoses, fireworks powder. 1060: Requires both corrosion resistance and formability of the occasi

Wrought aluminum and aluminum alloys can be divided into two types of cast aluminum. Wrought aluminum is not melted aluminum billet hot or cold forming; molten

Mechanical properties: Tensile strength σb (MPa): ≥430 Conditions yield strength σ0.2 (MPa): ≥275 Elongation δ5 (%): ≥10 Note: The

Features and Scope: Alloy rivets. With high shear strength and heat resistance, pressure processing performance and cutting performance and corrosion resistanc

2A06 aluminum alloy for high strength aluminum hard, pressure processing performance and cutting and 2A12 same, just in the annealed and quenched state plastic

Quenching and aging: hardening 530 ~ 540 ℃, water cooling; artificial aging (forgings, sheet) 160 ~ 170 ℃, 10 ~ 16h, air-cooled; natural aging at room temperature Anytime.

● Mechanical Properties Tensile strength σb (MPA): ≥315 Elongation δ5 (%): ≥4 Note: The vertical bar at room temperature mechanical properti

2A11 aluminum is the first application of a hard aluminum, commonly referred to as a standard hard aluminum.

2A10 aluminum alloys are the rivets. High shear strength, annealing, just quenching, aging and thermal state have sufficient plasticity rivet is required; with riveted after quenching and aging, the time limit is not heat-treated after the riveting proces

Alloy rivets. 2A02 shear strength and considerable, other properties and 2B11 similar, but rivets must be riveted within 20min after quenching, it is difficult to process, and thus the application range is limited

2A17 aluminum - copper - magnesium lines typical of the hard alloy, its composition is more reasonable, better overall performance. Many countries are producing

Belong to Al-Zn-Mg-Cu based hard aluminum alloy rivets. Quenching artificial aging state can be riveting, a high-strength rivets material when the temperature is below 100 ℃.

7A09 aluminum mechanical properties: Tensile strength σb (MPa): ≥530 Tensile stress σp0.2 (MPa): ≥400